Heraloy G (ราคาปรับตามราคาตลาดโลก)
Reduced Gold Ceramic Bonding Alloy (สีขาว)
acc. to EN ISO 9693-1 and 22674
ข้อได้เปรียบ
– ใช้งานได้ดีกับ single crown และ bridges ที่ขนาดยาวได้มากที่สุด
– ไม่มีส่วนประกอบของ Silver (Ag) และ Copper (Cu)
– ปริมาณ Oxide ต่ำ
– แต่ง Ceramic ได้ดี
– เหมาะกับการทำ PFM
– Functional composition
ประเภทงานที่เหมาะ
– Crowns
– Bridges
– Milling procedures
– Implants
แอดไลน์เพื่อสอบถามราคาและโปรโมชั่น
Add to Wishlist
Add to Wishlist
Description
Ceramic bonding alloy acc. to EN ISO 9693 EN ISO 22674 |
|
Type | 4 (s/ v/ k) |
Shade | White |
Indication | 3,4,5,15 |
Composition | Au 51.5 Pd 37.9 In 8.5 Ir x Ru x Ga 2.0 |
Technical specifications, melting and casting | |
Melting range | 1130 ° – 1280 ° C |
Preheating temperature | 900 ° C |
Casting temperature | 1430 ° C |
Crucible | Ceramic |
Density | 14.5 g/cm3 |
Hardness (HV5) | 250 (w/k), 260 (v), 210 (s) |
0.2 % yield strength (MPa) | 550 (w/k), 600 (v) |
Elongation (%) | 23 (w/k), 14 (v) |
Young’s modulus of elasticity (GPa) | 132 |
Ceramic firing | |
CTE | 13.9 |
Oxide firing | 880 ° C/ 5 min (stripping) |
Soft annealing | — |
Hardening | 650 ° C/ 15 min. |
Solder/laser welding wire | |
Solder | Herador solder 1070, 1060, 1060 S Herador solder V 800 |
Laser welding wires | Ø 0.5 mm x 200 mm + Ø 0.3 mm x 200 mm |
x = content < 0.1 mass%
Indications:
1 Inlays, cervical filling
2 MOD Inlays
3 Crowns
4 Bridges
5 Milling technique
6 Partial dentures
10 Cast posts
14 Can be veneered with high expansion, low-fusing ceramics
15 Implant restorations
16 Electroformed double crown technique (primary crowns)
1 Inlays, cervical filling
2 MOD Inlays
3 Crowns
4 Bridges
5 Milling technique
6 Partial dentures
10 Cast posts
14 Can be veneered with high expansion, low-fusing ceramics
15 Implant restorations
16 Electroformed double crown technique (primary crowns)
Footnotes:
w = after soft annealing and quenching
k = ceramic bonding alloy: condition after ceramic firing
v = after hardening
s = self-hardening after slow cooling in the mould
w = after soft annealing and quenching
k = ceramic bonding alloy: condition after ceramic firing
v = after hardening
s = self-hardening after slow cooling in the mould
A = A stable framework design with reinforced connections with a cross section of 8 – 10 mm² is required for long span bridges and superstructures. Additionally, the frameworks need to be hardened.
B = Depending on the copper content, in some cases discolouration ofdouble crowns may result after short period of wearing. Discolouration, however, is technically and physiologically harmless.
C = In exceptional cases these alloys can also be used for traditional telescopic crowns with parallel walls and for the bar casting technique provided that cross-sections for crown walls, approximal areas, bars and laser welded joints are particularly thick and the alloy is hardened subsequently. No indication for conical crowns and sheardistributors.
B = Depending on the copper content, in some cases discolouration ofdouble crowns may result after short period of wearing. Discolouration, however, is technically and physiologically harmless.
C = In exceptional cases these alloys can also be used for traditional telescopic crowns with parallel walls and for the bar casting technique provided that cross-sections for crown walls, approximal areas, bars and laser welded joints are particularly thick and the alloy is hardened subsequently. No indication for conical crowns and sheardistributors.